Superconducting electronics often require high-density microwave interconnects capable of transporting signals between temperature stages with minimal loss, cross talk, and heat conduction. We report the design and fabrication of superconducting 53 wt% Nb-47 wt% Ti (Nb47Ti) FLexible coAXial ribbon cables (FLAX). The ten traces each consist of a 0.076 mm O.D. NbTi inner conductor insulated with PFA (0.28 mm O.D.) and sheathed in a shared 0.025 mm thick Nb47Ti outer conductor. The cable is terminated with G3PO coaxial push-on connectors via stainless steel capillary tubing (1.6 mm O.D., 0.13 mm thick) soldered to a coplanar wave guide transition board. The 30 cm long cable has 1 dB of loss at 8 GHz with -60 dB nearest-neighbor forward cross talk. The loss is 0.5 dB more than commercially available superconducting coax likely due to impedance mismatches caused by manufacturing imperfections in the cable. The reported cross talk is 30 dB lower than previously developed laminated NbTi-onKapton microstrip cables. We estimate the heat load from 1 K to 90 mK to be 20 nW per trace, approximately half the computed load from the smallest commercially available superconducting coax from CryoCoax

Hafnium is an elemental superconductor which crystallizes in a hexagonal close packed structure, has a transition temperature $T_{C} \simeq 400 mK$, and has a high normal state resistivity around $90 \mu \Omega. cm$. In Microwave Kinetic Inductance Detectors (MKIDs), these properties are advantageous since they allow for creating detectors sensitive to optical and near infra-red radiation. In this work, we study how sputter conditions and especially the power applied to the target during the deposition, affect the hafnium $T_{C}$, resistivity, stress, texture and preferred crystal orientation. We find that the position of the target with respect to the substrate strongly affects the orientation of the crystallites in the films and the internal quality factor, $Q_{i}$, of MKIDs fabricated from the films. In particular, we demonstrate that a DC magnetron sputter deposition at a normal angle of incidence, low pressure, and low plasma power promotes the growth of compressive (002)-oriented films and that such films can be used to make high quality factor MKIDs with $Q_{i}$ up to 600,000.

We report on the design and performance of Microwave Kinetic Inductance Detectors (MKIDs) sensitive to single photons in the optical to near-infrared range using hafnium as the sensor material. Our test device had a superconducting transition temperature of 395 mK and a room temperature normal state resistivity of 97 $\mu \Omega$ cm with an RRR = 1.6. Resonators on the device displayed internal quality factors of around 200,000. Similar to the analysis of MKIDs made from other highly resistive superconductors, we find that modeling the temperature response of the detector requires an extra broadening parameter in the superconducting density of states. Finally, we show that this material and design is compatible with a full-array fabrication process which resulted in pixels with decay times of about 40 $\mu$s and resolving powers of ~9 at 800 nm.

Optical and near-IR Microwave Kinetic Inductance Detectors, or MKIDs, are superconducting photon counting detectors capable of measuring the energy and arrival time of individual OIR photons without read noise or dark current. In this whitepaper we will discuss the current status of OIR MKIDs and MKID-based instruments.