Xenon implantation into nanodiamonds is studied using molecular dynamics. The nanodiamonds range in size from 2-10 nm and the primary knock-on (PKA) energy extends up to 40 keV. For small nanodiamonds an energy-window effect occurs in which PKA energies of around 6 keV destroy the nanodiamond, while in larger nanodiamonds the radiation cascade is increasingly similar to those in bulk material. Destruction of the small nanodiamonds occurs due to thermal annealing associated with the small size of the particles and the absence of a heat-loss path. Simulations are also performed for a range of impact parameters, and for a series of double-nanodiamond systems in which a heat-loss path is present. The latter show that the thermal shock caused by the impact occurs on the timescale of a few picoseconds. These findings are relevant to ion-beam modification of nanoparticles by noble gases as well as meteoritic studies where implantation is proposed as the mechanism for xenon incorporation in pre-solar nanodiamonds.

Based on extensive laboratory characterization of presolar nanodiamonds extracted from mete-orites, we have proposed a novel approach to detect nanodiamonds at astrophysical objects using the 7370 {\AA} emission band arising from lattice defects. Details of laboratory spectroscopic studies and preliminary results of observations are presented.

Nanoparticles are ubiquitous in nature and are increasingly important for technology. They are subject to bombardment by ionizing radiation in a diverse range of environments. In particular, nanodiamonds represent a variety of nanoparticles of significant fundamental and applied interest. Here we present a combined experimental and computational study of the behaviour of nanodiamonds under irradiation by xenon ions. Unexpectedly, we observed a pronounced size effect on the radiation resistance of the nanodiamonds: particles larger than 8 nm behave similarly to macroscopic diamond (i.e. characterized by high radiation resistance) whereas smaller particles can be completely destroyed by a single impact from an ion in a defined energy range. This latter observation is explained by extreme heating of the nanodiamonds by the penetrating ion. The obtained results are not limited to nanodiamonds, making them of interest for several fields, putting constraints on processes for the controlled modification of nanodiamonds, on the survival of dust in astrophysical environments, and on the behaviour of actinides released from nuclear waste into the environment.

Photoluminescence spectra show that silicon impurity is present in lattice of some nanodiamond grains (ND) of various chondrites as a silicon-vacancy (SiV) defect. The relative intensity of the SiV band in the diamond-rich separates depends on chemical composition of meteorites and on size of ND grains. The strongest signal is found for the size separates enriched in small grains; thus confirming our earlier conclusion that the SiV defects preferentially reside in the smallest (less than 2 nm) grains. The difference in relative intensities of the SiV luminescence in the diamond-rich separates of individual meteorites are due to variable conditions of thermal metamorphism of their parent bodies and/or uneven sampling of nanodiamonds populations. Annealing of separates in air eliminates surface sp2-carbon, consequently, the SiV luminescence is enhanced. Strong and well-defined luminescence and absorption of the SiV defect is a promising feature to locate cold (< 250 {\deg}C) nanodiamonds in space.

Reflectance and emissivity spectra of nanodiamonds powder were measured in a dedicated setup at temperatures up to 873 K. The spectra are characterised by presence of sharp bands due to surface-bound functional groups. Thermal desorption of oxygen-containing groups lead to corresponding spectral changes. The maximal emissivity of nanodiamond powder reaches 0.985.

The results of spectroscopic and structural studies of phase composition and of defects in nanodiamonds from Efremovka (CV3) and Orgueil (CI) chondrites indicate that nitrogen atomic environment in meteoritic nanodiamonds (MND) is similar to that observed in synthetic counterparts produced by detonation and by the Chemical Vapour Deposition (CVD)-process. Most of the nitrogen in MND appears to be confined to lattice imperfections, such as crystallite/twin boundaries and other extended defects, while the concentration of nitrogen in the MND lattice is low. It is suggested that the N-rich sub-population of MND grains may have been formed with high growth rates in environments rich in accessible N (i.e., N in atomic form or as weakly bonded compounds). For the first time the silicon-vacancy complex (the "silicon" defect) is observed in MND by photoluminescence spectroscopy.