The dielectric properties of selected conductively-loaded polyimide samples are characterized in microwave through far infrared wavebands. These materials, belonging to the Vespel\textsuperscript{\textregistered} family, are more readily formed by direct machining than their ceramic loaded epoxy counterparts and present an interesting solution for realizing absorptive optical control structures. Measurements spanning a spectral range from 1 to 600\,${\rm cm^{-1}}$ (0.03 to 18\,THz) were preformed and used in parametrization of the media's dielectric function at frequencies below $\approx3\,$THz.

Recent advances in the physical vapor deposition (PVD) of protective fluoride films have raised the far-ultraviolet (FUV: 912-1600 {\AA}) reflectivity of aluminum-based mirrors closer to the theoretical limit. The greatest gains, at more than 20%, have come for lithium fluoride-protected aluminum, which has the shortest wavelength cutoff of any conventional overcoat. Despite the success of the NASA FUSE mission, the use of lithium fluoride (LiF)-based optics is rare, as LiF is hygroscopic and requires handling procedures that can drive risk. With NASA now studying two large mission concepts for astronomy, Large UV-Optical-IR Surveyor (LUVOIR) and the Habitable Exoplanet Imaging Mission (HabEx), which mandate throughput down to 1000 {\AA}, the development of LiF-based coatings becomes crucial. This paper discusses steps that are being taken to qualify these new enhanced LiF-protected aluminum (eLiF) mirror coatings for flight. In addition to quantifying the hygroscopic degradation, we have developed a new method of protecting eLiF with an ultrathin (10-20 {\AA}) capping layer of a non-hygroscopic material to increase durability. We report on the performance of eLiF-based optics and assess the steps that need to be taken to qualify such coatings for LUVOIR, HabEx, and other FUV-sensitive space missions.

The astronomical community continues to be interested in suitable programmable slit masks for use in multi-object spectrometers (MOSs) on space missions. There have been ground-based MOS utilizing digital micromirror devices (DMDs) and they have proven to be highly accurate and reliable instruments. This paper summarizes the results of a continuing study to investigate the performance of DMDs under conditions associated with space deployment. This includes the response of DMDs to radiation, to the vibration and mechanical shock loads associated with launch, and the operability of DMD under cryogenic temperatures. The optical contrast ratio and a study of the long-term reflectance of a bare device have also been investigated. The results of the radiation testing demonstrate that DMDs in orbit would experience negligible heavy-ion induced single event upset (SEU) rate burden, we predict SEU rate of 5.6 micromirrors per 24 hours. Vibration and mechanical shock testing was performed according to the NASA General Environmental Verification Standard (GEVS), no mirrors failed in the devices tested. The results of low temperature testing suggest that DMDs are not affected by the thermal load and operate smoothly at temperatures at least as low as 78 K. The reflectivity of a bare DMD did not measurably change even after being exposed to ambient conditions over a period of 13 months. The measured contrast ratio (on state vs off state of the DMD micromirrors) was greater than 6000/:1 when illuminated with an f/4 optical beam. Overall, DMDs are extremely robust and promise to provide a reliable alternative to micro shutter arrays (MSA) to be used in space as remotely programmable slit masks for MOS design.

The experimental investigation of a broadband far-infrared meta-material absorber is described. The observed absorptance is $>\,0.95$ from ${\rm 1-20\,THz}$ (${\rm 300-15\,\mu m}$) over a temperature range spanning ${\rm 5-300\,K}$. The meta-material, realized from an array of tapers ${\rm \approx 100\,\mu m}$ in length, is largely insensitive to the detailed geometry of these elements and is cryogenically compatible with silicon-based micro-machined technologies. The electromagnetic response is in general agreement with a physically motivated transmission line model.

The increasing scale of cryogenic detector arrays for sub-millimeter and millimeter wavelength astrophysics has led to the need for large aperture, high index of refraction, low loss, cryogenic refracting optics. Silicon with n = 3.4, low loss, and relatively high thermal conductivity is a nearly optimal material for these purposes, but requires an antireflection (AR) coating with broad bandwidth, low loss, low reflectance, and a matched coefficient of thermal expansion. We present an AR coating for curved silicon optics comprised of subwavelength features cut into the lens surface with a custom three axis silicon dicing saw. These features constitute a metamaterial that behaves as a simple dielectric coating. We have fabricated and coated silicon lenses as large as 33.4 cm in diameter with coatings optimized for use between 125-165 GHz. Our design reduces average reflections to a few tenths of a percent for angles of incidence up to 30 degrees with low cross-polarization. We describe the design, tolerance, manufacture, and measurements of these coatings and present measurements of the optical properties of silicon at millimeter wavelengths at cryogenic and room temperatures. This coating and lens fabrication approach is applicable from centimeter to sub-millimeter wavelengths and can be used to fabricate coatings with greater than octave bandwidth.

We present several corrections for point source photometry to be applied to data from the Infrared Array Camera (IRAC) on the Spitzer Space Telescope. These corrections are necessary because of characteristics of the IRAC arrays and optics and the way the instrument is calibrated in-flight. When these corrections are applied, it is possible to achieve a ~2% relative photometric accuracy for sources of adequate signal to noise in an IRAC image.