This paper presents highly precise measurements of thermal expansion of a "hybrid" carbon-fiber reinforced silicon carbide composite, HB-Cesic\textregistered - a trademark of ECM, in the temperature region of \sim310-10K. Whilst C/SiC composites have been considered to be promising for the mirrors and other structures of space-borne cryogenic telescopes, the anisotropic thermal expansion has been a potential disadvantage of this material. HB-Cesic\textregistered is a newly developed composite using a mixture of different types of chopped, short carbon-fiber, in which one of the important aims of the development was to reduce the anisotropy. The measurements indicate that the anisotropy was much reduced down to 4% as a result of hybridization. The thermal expansion data obtained are presented as functions of temperature using eighth-order polynomials separately for the horizontal (XY-) and vertical (Z-) directions of the fabrication process. The average CTEs and their dispersion (1{\sigma}) in the range 293-10K derived from the data for the XY- and Z-directions were 0.805$\pm$0.003\times10$^{-6}$ K$^{-1}$ and 0.837\pm0.001\times10$^{-6}$ K$^{-1}$, respectively. The absolute accuracy and the reproducibility of the present measurements are suggested to be better than 0.01\times10$^{-6}$ K$^{-1}$ and 0.001\times(10)^{-6} K^{-1}, respectively. The residual anisotropy of the thermal expansion was consistent with our previous speculation regarding carbon-fiber, in which the residual anisotropy tended to lie mainly in the horizontal plane.

We report on the microscopic surface structure of carbon-fiber-reinforced silicon carbide (C/SiC) composite mirrors that have been improved for the Space Infrared Telescope for Cosmology and Astrophysics (SPICA) and other cooled telescopes. The C/SiC composite consists of carbon fiber, silicon carbide, and residual silicon. Specific microscopic structures are found on the surface of the bare C/SiC mirrors after polishing. These structures are considered to be caused by the different hardness of those materials. The roughness obtained for the bare mirrors is 20 nm rms for flat surfaces and 100 nm rms for curved surfaces. It was confirmed that a SiSiC slurry coating is effective in reducing the roughness to 2 nm rms. The scattering properties of the mirrors were measured at room temperature and also at 95 K. No significant change was found in the scattering properties through cooling, which suggests that the microscopic surface structure is stable with changes in temperature down to cryogenic values. The C/SiC mirror with the SiSiC slurry coating is a promising candidate for the SPICA telescope.